Ceramic Fiber Blanket (MWOOL-BLANKET) is made of special ceramic fiber through special reinforced double-side needling process. Magscie reinforced double-sided needling process greatly improves the fiber interweaving as well as delamination resistance of ceramic fiber and makes blankets much stronger tensile strength without affecting its flexibility.
MWOOL -BLANKET has a clean white color and regular size, integrating fire resistance, thermal and insulation. It can be directly used as a flame hot surface, with a heat resistance temperature range of 1000-1600℃. Magscie MWOOL -BLANKET is produced without any binder. Therefore, it can maintain good tensile strength, toughness, and fiber structure even when used in a neutral and oxidizing atmosphere for a long time. And it can ensure the good reliability and stability no matter how high temperature and low temperature conditions.
MWOOL-BLANKET is chemically stable and resistant to most aggressive chemicals (except phosphoric acid, hydrofluoric acid and strong bases). Even if the product is soaked by oil, water or steam, its physical properties such as temperature resistance and heat insulation will not change.
MWOOL-BLANKET is soft and easy to install during construction. Using it instead of refractory brick lining can reduce weight by 80% and thickness by 50%. It can also effectively reduce fuel consumption, and industrial furnace energy consumption can be reduced by 26%~48%.
|
MAGSCIE |
ENWOOL -BLANKET 1000 |
ENWOOL -BLANKET 1260 |
ENWOOL -BLANKET 1430 |
ENWOOL -BLANKET 1500 |
ENWOOL -BLANKET 1600 |
|
|
Classicification Temperature |
oC |
1000 |
1260 |
1430 |
1500 |
1600 |
|
Properties measure at ambient condition (23oC/50% RH) |
||||||
|
Color |
|
White |
White |
White |
Green |
White |
|
Melting Point |
oC |
1700 |
1760 |
1700 |
1760 |
1840 |
|
Average Fiber Diameter |
μm |
2.6 |
2.6 |
2.8 |
2.65 |
3.10 |
|
Fiber Length |
mm |
~200 |
~250 |
~250 |
~150 |
~100 |
|
Average Gravity |
Kg/m3 |
2600 |
2600 |
2800 |
2650 |
3100 |
|
Shot Content (>212μm) |
% |
15 |
7 |
7 |
7 |
≤1 |
|
Permanent Linear Shrinkage 24h,128kg/m3 |
% |
≤2.0 900oC |
≤2.0 1100oC |
≤2.5 1300oC |
≤3.5 1400oC |
≤1.0 1600oC |
|
Tensile Strength, Thickness 25mm,128kg/m3. |
KPa |
40 |
80 |
80 |
80 |
103 |
|
Thermal Conductivity at mean temperature at 96 kg/m3 |
||||||
|
200oC 400oC 600oC 800oC 1000oC 1200oC |
W/M.K W/M.K W/M.K W/M.K W/M.K W/M.K |
0.06 0.10 0.18 0.27 – – |
0.06 0.10 0.18 0.27 0.36 – |
0.06 0.10 0.18 0.27 0.36 – |
0.06 0.10 0.18 0.27 0.36 – |
– 0.08 0.13 0.19 0.27 0.39 |
|
Thermal Conductivity at mean temperature at 128 kg/m3 |
||||||
|
200oC 400oC 600oC 800oC 1000oC 1200oC |
W/M.K W/M.K W/M.K W/M.K W/M.K W/M.K |
0.05 0.09 0.15 0.23 – – |
0.05 0.09 0.15 0.23 0.30 – |
0.05 0.09 0.15 0.23 0.30 – |
0.05 0.09 0.15 0.23 0.30 – |
– 0.08 0.12 0.17 0.24 0.33 |
|
Chemical Composition |
||||||
|
Al2O3 |
% |
42-44 |
45-47 |
34-36 |
41-43 |
72 |
|
SiO2 |
% |
56-58 |
53-55 |
49-51 |
54-56 |
28 |
|
ZrO2 |
% |
– |
– |
14-17 |
– |
– |
|
Cr2O3 |
|
– |
– |
– |
2-3 |
– |
Standard Size