Ceramic fiber paper (MWOOL-PAPER) is made of MWOOL through wet forming process. MWOOL-PAPER has uniform thickness, smooth surface, and good flexibility. It can be cut or punched to further produce products of various sizes and specifications.
MWOOL-PAPER has stable chemical properties and can resist the erosion of most chemical substances (except phosphoric acid, hydrofluoric acid and strong bases). Even if this series of products are wetted by oil, water or steam, their physical properties will not change after drying. Such as their temperature resistance and heat insulation. In addition, MWOOL-PAPER has excellent dielectric strength.
|
MAGSCIE |
MWOOL -PAPER 1000 |
MWOOL -PAPER 1260 |
MWOOL -PAPER 1400 |
|||||||
|
Classicification Temperature |
°C |
1000 |
1260 |
1400 |
||||||
|
Properties measure at ambient condition (23°C/50% RH) |
||||||||||
|
Color |
– |
White |
White |
White |
||||||
|
Bulk Density |
Kg/m3 |
210 |
210 |
210 |
||||||
|
Tensile Strength |
MPa |
0.50 |
0.65 |
0.65 |
||||||
|
Organic Content |
% |
≤10 |
≤8 |
≤8 |
||||||
|
Linear Shrinkage Rate |
% |
≤3.5 1000X24hrs |
≤3.5 1100X24hrs |
≤3.5 1200X24hrs |
||||||
|
Thermal Conductivity at mean temperature of |
||||||||||
|
200oC 400oC 600 oC 800oC 1000oC |
W/M.K W/M.K W/M.K W/M.K W/M.K |
0.05 0.09 0.13 0.20 – |
0.05 0.03 0.13 0.20 – |
0.05 0.09 0.13 0.20 0.28 |
||||||
|
Chemical Composition |
||||||||||
|
Al2O3 |
% |
42 |
45 |
35 |
||||||
|
SiO2 |
% |
54 |
54 |
48 |
||||||
|
ZrO2 |
% |
– |
– |
17 |
||||||